3255 Títúnṣe Diphenyl Ether Glassfiber Laminated Sheet
ọja Apejuwe
Ọja yii jẹ ọja ti a ti laini eyiti a ṣe pẹlu itọju kemikali itanna ti a pinnu alkali-free gilasi asọ bi ohun elo ti n ṣe afẹyinti, nipasẹ titẹ gbigbona pẹlu iyipada diphenyl ether resin bi binder.It ni agbara ẹrọ ti o ga labẹ temeprature giga, iduroṣinṣin dielectric ti o dara labẹ ọriniinitutu giga.Good Ìtọjú resistanceit, o dara fun kilasi H motor, ohun elo itanna bi awọn ẹya eto idabobo.
Awọn ẹya ara ẹrọ
1.High darí agbara labẹ ga otutu;
2.Good itanna iduroṣinṣin labẹ ọrinrin giga;
3.High ooru resistance;
4.High ọrinrin resistance;
5.Good machinability;
6.Good Ìtọjú resistance
7.Temperature resistance: Grade H
Ibamu Pẹlu Awọn ajohunše
Ni ibamu pẹlu GB/T 1303.4-2009 itanna thermosetting resini ise lile laminates - Apá 4: iposii resini lile laminates.
Ifarahan: oju yẹ ki o jẹ alapin, laisi awọn nyoju, awọn pits ati awọn wrinkles, ṣugbọn awọn abawọn miiran ti ko ni ipa lori lilo ni a gba laaye, gẹgẹbi: awọn fifọ, indentation, awọn abawọn ati awọn aaye diẹ.
Ohun elo
Dara fun motor kilasi H, ohun elo itanna bi awọn ẹya idabobo.
Main Performance Atọka
| RARA. | Nkan | UNIT | IYE index | ||
| 1 | iwuwo | g/cm³ | 1.8-2.0 | ||
| 2 | Oṣuwọn gbigba omi | % | ≤0.5 | ||
| 3 | Inaro atunse agbara | Deede | MPa | ≥340 | |
| 180±5℃ | ≥170 | ||||
| 4 | Agbara funmorawon | Inaro | MPa | ≥350 | |
| 5 | Agbara ipa (oriṣi charpy) | aafo | KJ/m² | ≥33 | |
| 6 | Agbara imora | N | ≥5700 | ||
| 7 | Agbara fifẹ | Ọna gigun | MPa | ≥300 | |
| 8 | Inaro ina agbara (ni epo ti 90 ℃ ± 2 ℃) | 1mm | KV/mm | ≥20.0 | |
| 2mm | ≥18.0 | ||||
| 3mm | ≥16.0 | ||||
| 9 | Foliteji didenukole ti o jọra (1 min ninu epo ti 90 ℃ ± 2 ℃) | KV | ≥30 | ||
| 10 | ifosiwewe dielectric pipinka (50Hz) | - | ≤0.04 | ||
| 11 | Ni afiwe idabobo Resistance | Deede | Ω | ≥1.0×1013 | |
| Lẹhin sisun fun wakati 24 | ≥1.0×1010 | ||||
| 12 | Volumn idabobo Resistance | Deede | Ω.m | ≥1.0×1011 | |
| Lẹhin sisun fun wakati 24 | ≥1.0×109 | ||||
| 180±5℃ | ≥1.0×108 | ||||